It’s a terrible idea on many levels. Large castings are very difficult, especially for odd shaped parts of varying thickness as you have to have the temperatures, feeds, breathers, etc. dialed in. IF you get your processes down finally, you have a single part that likely cannot be reworked if it doesn’t pass QA (this…